Hot / Cold Rolled Stainless Steel Coil 436L Cr 17% 2B BA Finish

1. Magnetic, ferritic stainless steel with low C, N contents and addition of Ti or Nb or Zr.
3. High thermal conductivity, low coefficient of thermal expansion, excellent formability and bendability.
4. Extra-high resistance to auto exhaust condensate corrosion and oxidation resistance, with elevated temperature strength.
5. No need for heat treatment after welding due to low C and the addition of Ti or Nb or Zr.

GRADE

400 SERIES, MAX, %

C

Mn

P

S

Si

Cr

Ni

Mo

N

Others

405

0.08

1.0

0.04

0.03

1.0

11.5-14.5

0.6

-

-

Al 0.10-0.30

409L

0.03

1.0

0.04

0.02

1.0

10.5-11.7

0.5

-

0.03

Ti 63(C+N) min,
0.50 max; Cb 0.17

410

0.08-0.15

1.0

0.04

0.03

1.0

11.5-13.5

0.75

-

-

-

410S

0.08

1.0

0.035

0.03

1.0

11.5-13.5

0.6

-

-

-

420J1

0.16-0.25

1.0

0.04

0.03

1.0

12.0-14.0

-

-

-

-

420J2

0.26-0.4

1.0

0.04

0.03

1.0

12.0-14.0

-

-

-

-

430

0.12

1.0

0.04

0.03

1.0

16.0-18.0

0.75

-

-

-

434

0.12

1.0

0.04

0.03

1.0

16.0-18.0

-

0.75-1.25

-

-

436L

0.25

1.0

0.04

0.03

1.0

16.0-19.0

-

0.75-1.25

-

Cb 53C min,0.80 max

439

0.03

1.0

0.04

0.03

1.0

17.0-19.0

0.5

-

0.03

Ti [0.20+4(C+N)]
min, 1.10 max; Al 0.15

443

0.025

1.0

0.04

0.03

1.0

20.0-23.0

0.5

-

0.025

(Ti+Cb)83(C+N) min,

0.80 max. Cu: 0.3-0.8

444

0.025

1.0

0.04

0.03

1.0

17.5-19.5

1

1.75-2.5

 

(Ti+Cb)[0.20+4(C+N)]
min,0.80 max; Cu≤0.035

447

0.01

0.3

0.025

0.02

0.2

28.0-30.0

0.15

3.5-4.2

0.02

(C+N) 0.025, Cu≤0.15